ALD of metal silicate films

ABSTRACT

Methods for forming metal silicate films are provided. The methods comprise contacting a substrate with alternating and sequential vapor phase pulses of a silicon source chemical, metal source chemical, and an oxidizing agent, wherein the metal source chemical is the next reactant provided after the silicon source chemical. Methods according to some embodiments can be used to form silicon-rich hafnium silicate and zirconium silicate films with substantially uniform film coverages on substrate surface.

REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Patent Application No. 60/850,082, filed Oct. 5, 2006. The present application is related to U.S. patent application Ser. No. 10/148,525 to Tois et al., filed May 31, 2002, U.S. patent application Ser. No. 10/678,766 to Tois et al., filed Oct. 3, 2003, and U.S. patent application Ser. No. 11/490,875 to Wang et al., filed Jul. 21, 2006. The entirety of each of the above-referenced applications is incorporated herein by reference and made part of this specification.

BACKGROUND

1. Field of the Disclosure

The present disclosure relates to metal silicate films. In particular, the disclosure concerns methods for forming silicon-rich metal silicate films by atomic layer deposition (ALD) and the films formed by such methods.

2. Description of the Related Art

The integration level of components in integrated circuits is increasing, which rapidly places a demand for a decrease of the size of integrated circuit (IC) components and interconnects. Design rules are setting the feature sizes to ≦0.2 μm, making complete film coverage on deep bottoms and vias difficult to obtain using traditional methods. Additionally, with decreasing feature sizes, quantum mechanical tunneling (“tunneling”) leads to leakage current, i.e., current leaking out of device features (e.g., across gate oxides), which adversely affects device performance. For this reason, substantially thin SiO₂ films are unreliable as gate dielectrics (gate oxides), for example, in MOSFET (metal-oxide-semiconductor field-effect transistor) devices. Thus, a dielectric material with a high dielectric constant (“high-k dielectric”) is desirable.

At least some high-k dielectric materials can be deposited on silicon surfaces and remain stable under thermal annealing processes. In gate dielectric applications, electrically active defects should be minimized or prevented from forming at interfaces between silicon wafers and high-k dielectrics. In memory applications, such as in dynamic random access memory (DRAM) applications, the structure of the dielectric can be substantially stable under high activation temperatures. It has been found that mixing silicon oxide (SiO_(x), where ‘x’=1 or 2) with a metal oxide forms stable metal silicates that can be used as high-k dielectrics with desirable properties.

Hafnium silicate (HfSiO_(x)) and Zirconium silicate (ZrSiO_(x)) have been used to replace silicon oxide in some applications, such as complementary metal oxide semiconductor (CMOS) applications, because they can offer excellent thermal stability and device performance in integrated circuits with device features sizes of about 65 nanometers (nm) or less. However, with decreasing features sizes, it has become increasingly difficult to deposit hafnium silicate films with compositional and thickness uniformities suited for current and future generation of ICs.

Metal silicate films are conventionally deposited by first contacting a substrate surface with water to form initial OH surface terminations, followed by contacting the substrate with a pulse of a metal source chemical (e.g., HfCl₄) to form a metallic film on the substrate, the metallic film comprising metals with halogen ligands (e.g., Si—O—HfCl₃). Subsequently contacting the metals with water replaces the halogen ligands with OH ligands. Next, a silicon source chemical (e.g., SiCl₄) is contacted with the OH terminated metals to form halogen terminated silicon atoms covalently bonded to the metals (e.g., Si—O—Hf—O—SiCl₃). Subsequent exposure to water replaces the halogen ligands with OH groups (e.g., Si—O—Hf—O—Si(OH)₃). This process can be repeated to form a metal silicate film. With decreasing device dimensions, metal silicate films with high dielectric constants are desirable because they will minimize quantum mechanical tunneling across the dielectric. Metal silicate films with increased silicon content are desirable because they have excellent thermal stability and good interface properties. However, a limitation of the conventional processes described above is that the maximum silicon content achievable is about 65%, rendering the method unsuitable for applications in which metal silicate films with a silicon content greater than 65% are desired.

SUMMARY

In one aspect, atomic layer deposition (ALD) methods for forming a metal silicate film are provided. The methods can include contacting a substrate in a reaction space with spatially and temporally separated vapor phase pulses of a silicon source chemical, a metal source chemical and an oxidizing agent, wherein the metal source chemical is the next reactant provided after the silicon source chemical. The metal silicate film may be a silicon-rich film. In some embodiments the metal source chemical is HfCl₄, the silicon source chemical is SiCl₄ and the oxidizing agent is H₂O.

In some embodiments, metal silicate films are deposited by an ALD process comprising (a) contacting the substrate with a vapor phase pulse of a silicon source chemical; (b) removing excess silicon source chemical and reaction by-products, if any, from the reaction space; (c) contacting the substrate with a vapor phase pulse of a metal source chemical; (d) removing excess metal source chemical; (e) contacting the substrate with a vapor phase pulse of an oxidizing agent; (f) removing excess oxidizing agent and reaction by-products, if any, from the reaction space; and (g) repeating steps (a) through (f) until a metal silicate film of predetermined thickness if formed on the substrate. The ALD process may begin with step (a). However, in some embodiments, the process may begin with a different step, such as step (c) or step (e). In some embodiments, the metal source chemical is the next reactant provided after the silicon source chemical. In some embodiments, step (a) and step (c) can be merged into one step where silicon source chemical and metal source chemical are introduced into the reaction space simultaneously. In addition, the substrate surface may be treated prior to beginning the first ALD cycle to provide an appropriate termination. For example the substrate may be terminated with OH groups, prior to beginning the ALD process.

In some embodiments a silicon-rich film is deposited by alternately contacting the substrate with a silicon source chemical such as SiCl₄ and an oxidizing agent, such as, for example, water, a number of times after step (f) and prior to beginning the primary ALD cycle again.

In another aspect, a silicon-rich metal silicate film is provided. In some embodiments, the silicon-rich metal silicon film has a silicon content greater than about 65%, greater than about 75%, or greater than about 80%.

All of these aspects are intended to be within the scope of the invention herein disclosed. Other embodiments of the present invention will be readily apparent to those skilled in the art from the following detailed description of some embodiments and reference to the attached FIGURE, the invention not being limited to any of the particular embodiments disclosed.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will be better understood from the Detailed Description and from the appended drawing, which is meant to illustrate and not to limit the invention.

FIG. 1 is a block diagram of a pulsing sequence according to an embodiment.

DETAILED DESCRIPTION

In conventional methods of depositing metal oxide films by atomic layer deposition (ALD), cycles depositing films of silicon oxide and metal oxide are alternated. The stoichiometry is controlled, as much as possible, by adjusting the ratio of cycles depositing the metal oxide, such as hafnium oxide, to cycles depositing silicon oxide. However, the commonly used silicon halide precursors are only able to initiate further SiO₂ growth under very high precursor partial pressure or with lengthy exposure. As a result, there is a limit to the amount of silicon that can be incorporated in the silicate film under commercially viable reaction conditions, even when the ratio of silicon oxide deposition cycles to metal oxide deposition cycles is high. In particular, under typical reaction conditions silicon incorporation saturates at around 65% because of the inability to grow additional layers of silicon oxide upon itself in a production-worthy time scale. While longer exposure to silicon halide precursors can be used to incorporate more silicon into the metal silicate film, the required exposure time slows down the process and reduces throughput to an unacceptable level. In order to avoid this problem, the art has generally looked to other more reactive precursors such as organic silicon precursors. However, there are a number of problems associated with the use of such precursors, including carbon contamination and degraded electrical properties.

The methods described herein enable formation of silicon-rich metal silicon films by limiting the amount of Hf incorporated into the growing film in each cycle, thus allowing for the incorporation of more silicon. This can be accomplished by providing the metal precursor pulse as the next reactant following the silicon precursor pulse in each ALD cycle. In some embodiments, the methods enable formation of a metal silicate film with a silicon content greater than 65%, greater than or equal to 75%, or greater than or equal to 80%. Although described primarily in terms of deposition of silicate films containing hafnium, the skilled artisan will recognize that the methods described herein can be applied to the formation of silicate films comprising other metals.

As used herein, “an ALD process” generally refers to a process for producing thin films over a substrate molecular layer by molecular layer using self-saturating chemical reactions. The general principles of ALD are disclosed, e.g., in U.S. Pat. Nos. 4,058,430 and 5,711,811, and Suntola, e.g., in the Handbook of Crystal Growth 3, Thin Films and Epitaxy, Part B: Growth Mechanisms and Dynamics, Chapter 14, Atomic Layer Epitaxy, pp. 601-663, Elsevier Science B.V. 1994, the entire disclosures of which are incorporated herein by reference. In a typical ALD process, gaseous reactants are conducted separately (usually alternately and sequentially) into a reaction space of an ALD type reactor where they contact a substrate located in the space to provide a surface reaction. The pressure and the temperature of the reaction space are adjusted to a range where physisorption (i.e., condensation of gases) and thermal decomposition of the precursors are avoided. In addition, reactants that do not react with themselves are selected. Consequently, only up to one monolayer (i.e., an atomic layer or a molecular layer) of material is deposited at a time during each pulsing cycle. The actual growth rate of the thin film, which is typically presented as Å/pulsing cycle, depends, for example, on the number of available reactive surface sites and the bulkiness of the reactant molecules. That is, once all available binding sites are filled, no additional surface reactions are possible. Gas phase reactions between precursors and any undesired reaction by-products are inhibited because reactant pulses are separated from each other by time and/or space. The reaction space is typically purged with an inert gas (e.g., N₂, Ar, He, or H₂) and/or evacuated, e.g., using a vacuum pump, between reactant pulses to remove excess gaseous reactants and reaction by-products, if any.

A reaction space can include a volume in a reactor in which conditions can be adjusted to effect film growth by ALD processes. The reaction space can include surfaces subject to all reaction gas pulses from which gases or particles can flow to the substrate, by entrained flow or diffusion, during normal operation. The reaction space can be, for example, the reaction chamber in a single-wafer ALD reactor or the reaction chamber of a batch ALD reactor, where deposition on multiple substrates takes place at the same time. In addition, chemical vapor deposition (CVD) reactors can be adapted for use in the methods. The reactor can be configured for plasma generation, either in situ or remote. An example reactor is the Pulsar™ reactor available from ASM America (Phoenix, Ariz.).

A metal silicate film is a film that includes silicon, one or more metals (other than silicon) and oxygen. A metal silicate film can be generally denoted by M_(x)Si_(y)O_(z), wherein “M” designates one or more metals and “x”, “y” and “z” are numbers greater than zero. A metal silicate film can be formed by depositing tiered and alternating layers of silicon oxide (e.g., SiO, SiO₂) and a metal oxide. As an example, a hafnium silicate film may be formed from alternating layers of HfO₂ and SiO₂. A silicon-rich metal silicate film can be formed by depositing tiered layers, wherein each layer may comprise a metal oxide and a silicon oxide (also referred to herein as a “mixed layer”). Metal silicate films with increased silicon content can be deposited directly on a silicon surface to achieve desirable electrical properties.

Silicon content in a film can be determined by dividing the total number of silicon atoms in a metal silicon film by the total number of silicon and metal atoms, i.e., Si/(Si+metal). Accordingly, the silicon content is average across a metal silicate film.

The methods presented herein allow controlled deposition of a conformal metal silicate films, such as, for example, silicon-rich metal silicate films, on a substrate surface. The substrate is a workpiece on which deposition is desired and can include silicon, silica, coated silicon, copper metal, dielectric materials, nitride, and/or combinations of materials. The substrate surface is a boundary between the reaction space and a feature of the substrate. Geometrically challenging applications, such as deposition in high aspect-ratio features (e.g., vias and trenches), are possible due to the self-limiting nature of the surface reactions using the chemistries provided herein.

According to some embodiments, ALD is used to form silicon-rich metal silicate films over a substrate, such as an integrated circuit (IC) workpiece. The substrate or workpiece is placed in a reaction space and subjected to alternately repeated surface reactions of a silicon source chemical, a metal source chemical and an oxidizing agent, where the metal source chemical is the next reactant provided after the silicon source chemical. Some ALD methods are “thermal” ALD processes, in which the substrate is heated during deposition. Alternatively, in some embodiments, plasma-enhanced ALD processes may be used.

In some embodiments, each ALD cycle comprises at least three deposition steps or phases and utilizes at least three different reactants. Although referred to as “the first,” the second,” and “the third” reactant, these designations do not imply that the reactants have to be introduced in this order. Thus, in some embodiments, an ALD cycle may start with the third reactant. Similarly, although referred to as first, second and third phases, they are not necessarily carried out in this sequence. For example, in some cases, deposition may start with the third phase. Additionally, each of the phases may be repeated prior to a subsequent phase. Additional phases, such as a silicon deposition phase, may also be incorporated into the overall ALD process.

In some embodiments, the first reactant (also referred to as “silicon reactant” herein) is a vapor phase silicon source chemical (also referred to as “silicon source material” or “silicon halide source chemical” herein) and will react with a substrate surface in a self-limiting manner to form no more than about one monolayer of silicon, provided that the substrate surface comprises the appropriate termination and/or bonding configuration.

In some embodiments, the silicon source chemical is a silicon halide compound, such as, e.g., Si_(x)W_(y)H_(z), wherein “W” is a halide selected from the group consisting of F, Cl, Br and I, “x” and “y” are integers greater than zero, and “z” is an integer greater than or equal to zero. The silicon halide source chemical may be selected from the group consisting of silicon fluorides (e.g., SiF₄), silicon chlorides (e.g., SiCl₄), silicon bromides (e.g., SiBr₄), and silicon iodides (e.g., SiI₄). In some embodiments, the silicon halide compound is silicon tetrachloride (SiCl₄).

The second reactant (also referred to as a “metal reactant” herein) is a metal source chemical and will react with unoccupied binding sites on the substrate surface. These unoccupied sites are generally sites that are not able to react with a previous silicon source chemical pulse, for example because of thermodynamic or kinetic considerations. No more than about one monolayer of a metal (or a plurality of metals if a source chemical comprising a plurality of metals is used, or if a plurality of metal source chemicals are used) is adsorbed on the substrate surface. Adsorption can include forming a chemical bond to the surface, or chemisoprtion or forming a weakly-bound condensed phase on the surface, or physisorption. The metal reactant can include a transition metal species desired in the metal silicate film being deposited. In particular embodiments, the metal reactant is a vapor phase species comprising one or both of hafnium (Hf) and zirconium (Zr).

The metal reactant is typically selected based on reactivity, vapor pressure and compatibility with the silicon reactant. In some embodiments, the metal reactant is a metal halide source chemical. In some embodiments, the metal reactant is MX₄, wherein “M” is a metal, such as, e.g., Hf or Zr, and X is selected from the group consisting of F, Cl, Br and I. An example reactant is HfCl₄.

The third reactant (also referred to as an “oxidizing agent” or “OH-contributing agent” herein) comprises oxygen and, in some embodiments, comprises an OH group. In some embodiments, the oxidizing agent is capable of contributing OH groups to silicon and/or metal on the substrate surface. The oxidizing agent is typically a vapor phase species of, for example, water (H₂O), hydrogen peroxide (H₂O₂), O₂, O₃, D₂O, D₂O₂, N₂O, NO, N₂O₅, and plasma-activated species of oxygen. The oxidizing agent can also be an alcohol, such as, for example, isopropyl alcohol, methanol, ethanol, a small molecular weight alcohol, or another suitable organic compound having a hydroxyl group. In some embodiments, the oxidizing agent is an NO_(x)-type of neutral species or oxygen-containing radicals. In some embodiments, the oxidizing agent reacts with silicon and/or a metal on a substrate surface to form a silicon/metal hydroxide.

It will be appreciated that prior to deposition of a metal silicate film, the substrate may be provided with an initial surface termination. As an example, a silicon substrate may be contacted with water to form an OH surface termination on the silicon. The surface termination may, for example, make the surface reactive with one of the metal or silicon reactants.

In one phase of the ALD cycle, herein referred to as “the first phase,” after initial surface termination, if desired, a pulse of the silicon reactant (i.e., silicon source chemical) is supplied to the reaction space. The amount of silicon source chemical that can adsorb on the surface is determined at least in part by the number of available binding sites on the surface and by steric constraints. The silicon reactant will react with —OH terminated surface sites on the substrate surface, if the energy barrier for the ligand exchange reaction can be overcome under the reaction conditions. However, at the deposition temperature and with a practical and commercially viable pulse duration, the silicon reactant will not react with all —OH terminated sites on the substrate surface due to the thermodynamic and kinetic considerations. As a result, there will still be unoccupied surface groups with specific bonding structure.

The silicon source chemical, which, in some embodiments, is a silicon halide source chemical (e.g., SiCl₄), can be provided with the aid of an inert carrier gas (e.g., N₂, He, Ar) or on its own (so-called vapor draw scheme). Due to the size of the species and the number of reactive sites, less than a monolayer (ML) is typically deposited in each pulse of the silicon source chemical. The chemisorbed layer left by the pulse of the silicon source chemical is self-terminated with a surface that is non-reactive with the remaining chemistry of that pulse. This phenomenon is referred to herein as “self-saturation” and the adsorption of silicon reactant is thus self-limiting.

Excess silicon source chemical and reaction by-products (if any) are removed from the reaction space, for example with the aid of a purge gas (e.g., N₂, He, Ar) and/or a vacuum generated by a pumping system. If the silicon source chemical is supplied with the aid of a carrier gas, excess silicon source chemical and reaction by-products may be removed by terminating the flow of the silicon source chemical and continuing to supply the carrier gas. In this respect, the carrier gas serves as the purge gas.

In the next phase of the ALD cycle, herein referred to as the “second phase,” the metal reactant (i.e., metal source chemical) is provided into the reaction space. The metal source chemical, which, in some embodiments, is a halogen-containing metal source chemical (e.g., HfCl₄), can be provided with the aid of an inert carrier gas. The metal source chemical is able to react at unoccupied binding sites on the substrate surface comprising an appropriate functional group. Such binding sites may be available for reaction with the metal source chemical because they are not able to react with the previous silicon source chemical pulse for thermodynamic or kinetic reasons. The amount of metal source chemical that can adsorb on the surface is thus determined at least in part by the number of available and suitable binding sites on the surface and by steric constraints. For example, previously adsorbed silicon halide may sterically prevent the metal reactant from reacting at all possible binding sites.

Again, due to the size of the chemisorbed species and the number of reactive sites, less than a monolayer (ML) is typically deposited in each pulse of the metal source chemical. As with the silicon source chemical, the chemisorbed layer left by the pulse of the metal source chemical is self-terminated with a surface that is non-reactive with the remaining chemistry of that pulse. Thus, the adsorption of metal reactant is also self-limiting. A film with more than one type of metal can be formed by adding additional metal phases.

Excess metal reactant and reaction by-products (if any) are removed from the reaction space. This step may include terminating the pulse of the metal reactant and purging the reaction space with an inert gas (e.g., N₂, He, Ar) and/or pumping the reaction space with the aid of a pumping system. If the metal reactant is supplied with the aid of a carrier gas, excess metal reactant and reaction by-products, if any, may be removed by terminating the flow of the metal reactant and continuing to supply the carrier gas.

In the next phase of the ALD cycle, herein referred to as the “third phase” or “oxidizing phase,” a pulse of the third reactant, an oxidizing agent, is provided into the reaction space. The oxidizing agent may be introduced on its own or with the aid of a carrier gas. The oxidizing agent reacts with the available metal and/or silicon on the substrate surface to form metal and/or silicon oxide on the substrate surface.

Excess oxidizing agent and reaction by-products, if any, are removed from the reaction space, for example by purging with an inert gas and/or by pumping the reaction space with the aid of a pumping system after stopping the flow of the oxidizing agent.

As mentioned above, it will be appreciated that alternatives to the sequence of steps outlined above are possible. As an example, the cycle may begin with the third phase (provision of the oxidizing agent), or with the second phase (provision of the metal reactant). However, in some embodiments, the metal reactant is the next reactant provided after the silicon reactant. Thus, in some embodiments, a pulsing sequence may include the following sequence of reactant pulses: silicon reactant pulse/metal reactant pulse/oxidizing agent pulse. In other embodiments, the reactant pulses may initiate with an oxidizing agent pulse. As an example, the reactant pulses may include the following sequence of pulses: oxidizing agent pulse/silicon reactant pulse/metal reactant pulse. One of skill in the art will appreciate that because of the cyclical nature of the process, these cycles primarily differ in the first cycle in the ALD process.

In some embodiments, the reactant pulses are separated by a removal step, in which excess reactants and/or reaction by-products (if any) are removed from the reaction space. Removal of excess reactants and/or by-products can occur, for example, with the aid of a purge gas and/or a pumping system, as described above.

It will be appreciated that each of the phases (either in combination with another phase or individually) may be repeated a predetermined number of times prior to the other phases. This can allow control of the stoichiometry of the metal silicate film being formed. For example, if a metal-rich metal silicate film is desired, the second (metal) and third (oxidizing) phase may be repeated several times prior to the silicon oxide phase. On the other hand, if a silicon-rich metal silicate film is desired, the first (silicon) and third (oxidizing) phases can be repeated a number of times prior to continuing with the regular cycle (first through third phases).

In some embodiments, a primary pulsing sequence is oxidizing agent/silicon reactant/metal reactant. This pulsing sequence can be repeated to produce a metal silicate film with a silicon content of about 60 at %.

To increase the silicon concentration further, a secondary reactant pulsing cycle of silicon reactant/oxidizing agent can be repeated one or more times prior to repeating the primary cycle of silicon reactant/metal reactant/oxidizing agent. The secondary pulsing cycle can be repeated any number of times prior to repeating the primary cycle. In some embodiments the secondary cycle is repeated one or more times, five or more times, or some other suitable number of times prior to beginning the primary cycle again. In this way a silicon-rich metal silicate film can be produced with a silicon concentration of greater than 60 at %. In some embodiments the secondary cycle is repeated five times for every primary cycle to produce a silicon-rich metal silicate film with a silicon concentration of above 80 at %. In other embodiments the primary cycle may be repeated multiple times for every secondary cycle.

The skilled artisan will be able to adjust the ratio of the various phases to produce films with stoichiometries suitable for various electronics applications.

A reactant is considered to immediately follow another reactant if only a purge or other reactant removal step intervenes.

In one embodiment, a primary ALD cycle for forming a metal silicate on a substrate comprises:

1. providing a vapor phase pulse of an oxidizing agent to the reaction space, such as, for example, H₂O;

2. purging and/or evacuating excess oxidizing agent and reaction by-products from the reaction space;

3. providing a vapor phase pulse of an silicon halide source chemical to the reaction space, such as, for example, SiCl₄;

4. purging and/or evacuating excess silicon source chemical and reaction by-products from the reaction space;

5. providing a vapor phase pulse of a metal source chemical to the reaction space, such as, for example, HfCl₄; and

6. purging and/or evacuating excess metal source chemical and reaction by-products from the reaction space.

Thus, in one complete primary ALD cycle for depositing a metal silicate on a silicon substrate, formation of the metal silicate film proceeds via formation of an —OH terminated silicon layer on the substrate. However, as SiCl₄ is not strongly reactive with —OH terminated surface groups at the deposition temperature, there is limited adsorption of silicon on the substrate during the first silicon halide reactant pulse (3). The metal source chemical provided in the subsequent pulse (5) is able to react with the surface functional groups at unoccupied binding sites and a layer of metal is adsorbed on the substrate.

The cycle is repeated such that the oxidizing agent is provided again (1) and is able to react with the adsorbed metal to form an oxide and, in some embodiments, an OH-terminated metal layer. The silicon halide reactant (2) is able to react with the available binding sites (for example, OH-terminated sites), leaving a surface comprising silicon (halide terminated, not OH-terminated) and some unoccupied surface groups. The metal halide pulse (3) reacts with the available surface groups, but is not able to react with the halide-terminated silicon (which does not have an —OH termination). Finally, the oxidizing agent is able to react with the adsorbed silicon halide and the adsorbed metal halide. The cycle is repeated to form a metal silicate film of desired thickness.

As mentioned above, by adding an additional secondary cycle comprising alternating and sequential provision of silicon halide and water, additional silicon can be incorporated into the growing film. In some embodiments, the secondary cycle is repeated from 1 to 10 or more times for each primary cycle. In some embodiments, the secondary cycle is repeated 5 times for each primary cycle.

The substrate temperature and/or reaction space pressure can be selected to optimize growth of the metal silicate film. In some embodiments, films are formed at a substrate temperature between about 150° C. and 500° C., between about 250° C. and 350° C., or at another suitable temperature. In some embodiments, the pressure of the reaction space during formation of the metal silicate film is between about 0.1 and 100 Torr, between about 0.5 and 10 Torr, or another suitable pressure.

An exemplary pulsing sequence according to methods of some embodiments is illustrated in FIG. 1. In the illustrated embodiment, the metal silicate film being formed is hafnium silicate. It will be appreciated, however, that these methods can be applied to forming metal silicate films comprising other metals, such as zirconium, in which case the metal source chemical used can be selected as described above.

With reference to FIG. 1, after initial surface termination, if necessary or desired, an oxidizing reactant or source material is supplied 102 into the reaction space comprising the substrate. In the illustrated embodiment, the oxidizing reactant is H2O. The H2O may be provided with the aid of a carrier gas or on its own.

Next, excess oxidizing reactant is removed 104 from the reaction space. Step 104 may entail stopping the flow of the reactant while continuing to flow a carrier gas for a sufficient time to diffuse or purge excess reactants and reaction by-products from the reaction space. For other embodiments, the purge gas is different from the carrier gas. In such a case, the carrier gas serves as the purge gas during the reactant removal step 104. In some embodiments, the removal 104 comprises flowing a purge gas for between about 0.1 seconds and 20 seconds after stopping the flow of the metal reactant pulse. Inter-pulse purging is described, for example, in U.S. Pat. No. 6,511,539, filed Sep. 8, 1999, entitled, “Apparatus and Method for Growth of a Thin Film,” the entire disclosure of which is incorporated herein by reference. In some arrangements, the reaction space may be pumped down between alternating chemistries. See, for example, PCT publication number WO 96/17107, published Jun. 6, 1996, entitled “Method and Apparatus for Growing Thin Films,” the entire disclosure of which is incorporated herein by reference. Thus, the removal step 104 may entail simultaneously purging and pumping the reaction space. Together, the provision 102 and removal 104 of H2O represent a first phase 120 of the illustrated ALD cycle.

Next, SiCl₄ is pulsed 106 to the substrate. After a time period sufficient to react with the surface (if the appropriate termination is present), the SiCl₄ pulse is terminated and excess reactant and any reaction by-products are removed 108 from the reaction space, for example, with the aid of a purge gas pulse and/or a vacuum generated by a pumping system. The removal step 108 may be as described for step 104 above. Together, steps 106 and 108 represent a second phase 130 of the illustrated ALD process.

Next, HfCl₄ is supplied 110 to the substrate. In accordance with some embodiments, the HfCl₄ pulse 110 is the next reactant pulse following the SiCl₄ pulse 106. The HfCl₄ reactant pulse 110 reacts with any available binding sites and leaves no more than a monolayer of a hafnium-containing film on the substrate.

Excess hafnium reactant and reaction by-products, if any, are removed 112 from the reaction space. As with removal step 104 above, step 112 can include stopping the flow of the third chemistry (HfCl₄) and continuing to flow carrier gas for a time period sufficient to remove excess reactants and any reaction by-products from the reaction space. Together, the hafnium reactant pulse 110 and removal step 112 represent a third phase 140 of the illustrated ALD process.

The first phase 120, second phase 130 and third phase 140 are repeated 160 until a hafnium silicate film of desired thickness is formed on the substrate. For example, the three phases may be repeated 10 times, 100 times, 1000 times or more to form a compositionally uniform hafnium silicate film.

In another alternative embodiment (not shown), the ALD sequence illustrated in FIG. 1 begins with the second phase 130 and is sequentially followed by the the third phase 140 and the first phase 120. In such a case, the sequence of steps includes: silicon source chemical pulse/reactant removal/metal source chemical pulse/reactant removal/oxidizing species pulse/reactant removal. This sequence may be repeated until a hafnium silicate film of desired thickness is formed on the substrate. As a particular example, a hafnium silicate film may be formed by an ALD cycle comprising the following vapor phase pulsing sequence: SiCl₄/inert gas/HfCl₄/inert gas/H₂O/inert gas.

In another alternative embodiment (not shown), the ALD sequence illustrated in FIG. 1 begins with the first phase 120 and is sequentially followed by a phase that includes at least some portions of the second phase 130 and the third phase 140. For example, after removal of excess oxidizing agent (104), silicon source chemical and metal source chemical can be introduced simultaneously. Excess silicon source chemical, metal source chemical, and reaction byproducts can subsequently be removed from the reaction space. As a particular example, a hafnium silicate film may be formed by an ALD cycle including the following vapor phase pulsing sequence: H₂O/inert gas/SiCl₄ and HfCl₄/inert gas.

Metal silicate films formed according to some methods have thicknesses between about 0.5 and 40 nm, between about 1 and 15 nm, or other suitable thicknesses. It will be understood that thicknesses can vary with application. For example, in gate dielectrics for CMOS devices, the metal silicate films can have thicknesses between about 1 and 5 nm. As another example, in DRAM devices, the metal silicate films can have thicknesses between about 3 and 15 nm. The skilled artisan will be able to select an appropriate thickness for a particular application.

Thus, according to the foregoing embodiments, a metal silicate film is formed on a substrate. Depending on their desired use, metal silicate films are formed having dielectric constants, for example, between about 4 and 50, between about 8 and 30, or other suitable dielectric constants. Metal silicate films formed according to methods described herein can have halogen (e.g., chlorine) impurity concentrations less than or equal to about 20,000 parts-per-million (ppm), less than or equal to about 10,000 ppm, less than or equal to about 5,000 ppm, or less than or equal to about 2,000 ppm.

In addition, metal silicate films formed according to methods described herein can have “within wafer” (WIW) uniformities (1 sigma) of less than about 1% on surfaces. In some embodiments, leakage current densities are less than or equal to about 1×10⁻³ A/cm² at an effective oxide thickness (EOT) of about 1.5 nm, less than or equal to about 1×10⁻⁴ A/cm² at an EOT of about 1.5 nm, or less than or equal to about 1×10⁻⁵ A/cm2 at an EOT of about 1.5 nm. Metal silicate films formed according to methods described herein can have metal and silicon concentrations between about 10% metal/90% Si to about 90% metal/10% Si.

The aforesaid embodiments will be further illustrated in the context of an example, which is not intended to limit the scope of the invention.

Example 1

A hafnium silicate film was deposited on a 300 mm silicon wafer using a Pulsar™ reactor manufactured by ASM America, Inc. Deposition was conducted at a substrate temperature in the range of about 300 to 350° C. The sequence processing steps included the following:

(1) H₂O pulse;

(2) N₂ purge;

(3) SiCl₄ pulse;

(4) N₂ purge;

(5) HfCl₄ pulse; and

(6) N₂ purge.

Steps (1)-(6) were repeated until a hafnium silicate film with a thickness of about 40 Å was formed on the silicon wafer.

In at least some of the aforesaid embodiments, any element used in an embodiment can interchangeably be used in another embodiment unless such a replacement is not feasible.

It will be appreciated by those skilled in the art that various other omissions, additions and modifications may be made to the methods and structures described above without departing from the scope of the invention. All such modifications and changes are intended to fall within the scope of the invention, as defined by the appended claims. 

1. An atomic layer deposition (ALD) method for forming a metal silicate film, the method comprising a plurality of cycles, each cycle comprising contacting a substrate in a reaction space with spatially and temporally separated vapor phase pulses of a silicon halide source chemical, a metal source chemical, and an oxidizing agent, wherein the metal source chemical is the next reactant provided after the silicon halide source chemical, wherein the metal silicate film has a silicon content greater than about 65 atomic %.
 2. The method of claim 1, further comprising purging the reaction space between each of said vapor phase pulses.
 3. The method of claim 1, wherein the silicon halide source chemical is SiCl₄.
 4. The method of claim 1, wherein the metal source chemical is a metal halide source chemical.
 5. The method of claim 4, wherein the metal source chemical comprises Hf or Zr.
 6. The method of claim 4, wherein the metal source chemical is HfCl₄.
 7. The method of claim 1, wherein the oxidizing agent comprises an agent selected from the group consisting of isopropyl alcohol, methanol, ethanol, a small molecular weight alcohol, NO, N₂O, N₂O₅, oxygen-containing radicals, H₂O, H₂O₂, O₂, O₃, D₂O, and D₂O₂.
 8. The method of claim 1, wherein the metal silicate film is formed at a substrate temperature of about 150° C. to about 500° C.
 9. The method of claim 8, wherein the metal silicate film is formed at a substrate temperature of about 200° C. to about 450° C.
 10. The method of claim 1, wherein the metal silicate film is used in a dynamic random access memory (DRAM) device.
 11. The method of claim 1, wherein the metal silicate film is used as a gate dielectric in a complementary metal oxide semiconductor (CMOS) device.
 12. An atomic layer deposition (ALD) method for forming a hafnium silicate film on a substrate in a reaction space, comprising the sequential steps of: (a) contacting the substrate with a vapor phase pulse of an oxidizing agent; (b) removing excess oxidizing agent and reaction by-products, if any, from the reaction space; (c) contacting the substrate with a vapor phase pulse of a silicon halide; (d) removing excess silicon halide and reaction by-products, if any, from the reaction space; (e) contacting the substrate with a vapor phase pulse of a metal halide; (f) removing excess metal halide and reaction by-products, if any, from the reaction space; and (g) repeating steps (a) through (f) until a metal silicate film of a desired thickness is formed on the substrate, wherein no reactant is provided between steps (c) and (e), and wherein the metal silicate film has a silicon content greater than about 65 atomic %.
 13. The method of claim 12, further comprising providing an initial surface termination on the substrate prior to contacting the substrate with the vapor phase pulse of the metal source chemical.
 14. The method of claim 12 additionally comprising a secondary cycle after step (f) and prior to step (g), the secondary cycle comprising providing alternately and sequentially a vapor phase pulse of silicon halide and a vapor phase pulse of an oxidizing agent.
 15. The method of claim 14, wherein the secondary cycle is repeated five times prior to step (g). 